xxizzer421xx · 01-19-2008, 10:24 PM

Well I have just recently decided on trying to pick up the art of brazing. And i decided to document my progress. I just did my first of brazing tonight, and just did a little messing around. It is definitely nothing fancy but it was fun just putting together nothing

Cloak · 01-19-2008, 11:46 PM

Yup, looks like first timer booger brazes we all did (and still do) heh.

Have fun, you'll start thinking of loads of different things you can braze together now.

Robb · 01-19-2008, 11:59 PM

Now you need a "XxIzzer421xX's Grinding Progress" thread.

As stated, we have all been there. There seems to be a lot of brazing material on your joints. A truly proper joint would show material that "flowed" into the base material, and what brazing material that remaining would be smooth and contour to the angles of the joint.

Just a couple of pointers as you progress:
-may try heating the base material up a little more. When hot enough, the brazing rod will flow. If it doesn't flow, back off with the rod and continue to heat the base material more.
-don't force the brazing rod in there. Once again, it will liquefy and flow when done properly.

For a first timer, your work looks abut right. And you are doing it right by just practicing on some scrap. Just keep cutting some short pieces and work on joining them as you are.............the technique will catch on.

Nice job so far, all you need is experience!

edit: are you brazing directly on that steel base (possibly drillpress)? If so, and your base material is in direct contact with that base, the base may be acting as a heatsink and constantly cooling down your tubing.

xxizzer421xx · 01-20-2008, 12:07 AM

No I just took the pictures On the press. You are exactly rite. I am kinda forcing the rod onto the metal, by pushing on it to try and get it to melt. The rod i have seems to have a very high melting point to it, when i out tomorrow i will just try heating it up alot and brazing with out forcing at all thanks for the help

mrpink · 01-20-2008, 09:15 AM

more heat, less braze.

p!nK

xxizzer421xx · 01-20-2008, 09:55 AM

thanks for your advice i will keep it in mind when i go out today and do some more

01-19-2008, 10:24 PM	#1
xxizzer421xx Rock Crawler Join Date: Feb 2007 Location: dexter Posts: 503	XxIzzer421xX's Brazing Progress Well I have just recently decided on trying to pick up the art of brazing. And i decided to document my progress. I just did my first of brazing tonight, and just did a little messing around. It is definitely nothing fancy but it was fun just putting together nothing

01-19-2008, 11:59 PM	#3
Robb RCC Addict Join Date: Aug 2005 Location: VARCOR Posts: 1,826	Now you need a "XxIzzer421xX's Grinding Progress" thread. As stated, we have all been there. There seems to be a lot of brazing material on your joints. A truly proper joint would show material that "flowed" into the base material, and what brazing material that remaining would be smooth and contour to the angles of the joint. Just a couple of pointers as you progress: -may try heating the base material up a little more. When hot enough, the brazing rod will flow. If it doesn't flow, back off with the rod and continue to heat the base material more. -don't force the brazing rod in there. Once again, it will liquefy and flow when done properly. For a first timer, your work looks abut right. And you are doing it right by just practicing on some scrap. Just keep cutting some short pieces and work on joining them as you are.............the technique will catch on. Nice job so far, all you need is experience! edit: are you brazing directly on that steel base (possibly drillpress)? If so, and your base material is in direct contact with that base, the base may be acting as a heatsink and constantly cooling down your tubing. Last edited by Robb; 01-20-2008 at 12:03 AM.

01-19-2008, 11:46 PM	#2
Cloak I wanna be Dave Join Date: Jan 2006 Location: Albuquerque Posts: 2,206	Yup, looks like first timer booger brazes we all did (and still do) heh. Have fun, you'll start thinking of loads of different things you can braze together now.

01-20-2008, 12:07 AM	#4
xxizzer421xx Rock Crawler Join Date: Feb 2007 Location: dexter Posts: 503	No I just took the pictures On the press. You are exactly rite. I am kinda forcing the rod onto the metal, by pushing on it to try and get it to melt. The rod i have seems to have a very high melting point to it, when i out tomorrow i will just try heating it up alot and brazing with out forcing at all thanks for the help

01-20-2008, 09:15 AM	#5
mrpink RCC Addict Join Date: Aug 2006 Location: trying to find out what a TVuPer is..... Posts: 1,851	more heat, less braze. p!nK

01-20-2008, 09:55 AM	#6
xxizzer421xx Rock Crawler Join Date: Feb 2007 Location: dexter Posts: 503	thanks for your advice i will keep it in mind when i go out today and do some more

Sponsored Links

RCCrawler Forums

Thread: XxIzzer421xX's Brazing Progress